QSW (Quick Shrink Wrap) Adhesive-Lined Polyolefin Wraparound Repair Sleeve R P W Table 1: Dimensions Size Substrate Diameter Dimension P Dimension R Range +1 mm (0.04 in.), - 0 6 mm (0.24 in.) mm (in.) mm (in.) mm (in.) QSW-60-100 10 (0.4) 20 (0.8) 60 (2.4) 100 (4.0) QSW-60-200 20 (0.8) 50 (2.0) 60 (2.4) 200 (7.9) QSW-60-300 40 (1.6) 75 (3.0) 60 (2.4) 300 (11.8) QSW-60-400 50 (2.0) 100 (4.0) 60 (2.4) 400 (15.7) QSW-100-100 10 (0.4) 20 (0.8) 100 (4.0) 100 (4.0) QSW-100-200 20 (0.8) 50 (2.0) 100 (4.0) 200 (7.9) QSW-100-300 40 (1.6) 75 (3.0) 100 (4.0) 300 (11.8) Notes: 1. Dimension W (wall thickness): 0.65 mm (0.025 in.) nominal 2. Dimension R (length of sheet) shrinks approximately 10% Material: QSW sleeves shall be fabricated from irradiated modified polyolefin compounded to produce a homogeneous, uniform product whose exterior surface is essentially free from flaws, defects, pinholes, seams, cracks or inclusions, and the color shall be black. The interior shall be coated with a hot melt thermoplastic adhesive. OBSOLETE 2007,2011 Tyco Electronics Corporation, a TE Connectivity Ltd. Company. All Rights Reserved. Customer Drawing Title: Raychem TE Connectivity QSW (Quick Shrink Wrap) Tubing 305 Constitution Drive Adhesive-Lined Polyolefin NOT the LATEST Menlo Park, CA 94025 USA Wraparound Repair Sleeve TE Connectivity reserves the right to amend this drawing at any time. Users Document No : should evaluate the suitability of the product for their application. QSW REVISION Cage Code: Scale: Size: Rev. Date: Rev: Sheet: 06090 None A 15-Apr-11 B1 1 of 2 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision. Table 2: Properties Property Unit Requirement Test Method Tensile Strength psi (MPa) 2466 (17) minimum ASTM D412 Ultimate Elongation percent 350 minimum ASTM D412 Specific Gravity - - - 1.05 maximum ASTM D792 Hardness shore D 40-50 ASTM D2240 Accelerated Aging ASTM D2671 168 hrs 150 2C (302 4F) followed by tests for: Tensile Strength psi (MPa) 1740 (12) minimum ASTM D412 Ultimate Elongation percent 200 minimum ASTM D412 Low Temperature Flexibility ASTM D2671 --- No cracking 4 hrs -40 3C (-40 5F) Procedure C Dielectric Strength V/mil (kV/cm) 500 (200) minimum ASTM D2671 12 Volume Resistivity ohm-cm 1 x 10 minimum ASTM D2671 Water Absorption percent 0.2 maximum ASTM D2671 168 hrs 23 2C (73 4F) Fluid Resistance AMS-DTL-23053/5 24 hours 23 2C (73 4F) in: Hydraulic Fluid (MIL-H-5606) JP-8 (MIL-T-5624) Lubricating Oil (MIL-L-7808) Lubricating Oil (MIL-L-23699) 5 percent NaCl (A-A-694) Deicing Fluid (MIL-A-8243) Skydrol 500 Followed by tests for: Tensile Strength psi (MPa) 1000 (6.9) minimum ASTM D412 Dielectric Strength V/mil (kV/mm) 400 (15.8) minimum ASTM D2671 Weathering The material from which QSW is manufactured contains carbon black to protect it from ultraviolet radiation. Acceptance Tests: 1. Dimensional (1 piece per lot): Shall meet the specified dimensions. 2. Visual (20 pieces per lot): Both backing and adhesive surfaces shall be essentially free from flaws, defects, pinholes, seams or cracks, and must have clean cut edges. 3. Application (1 piece per lot): 15 minutes 175 2C No slip page, bubbles or flaws. Customer Drawing Rev. Date: Rev.: Document No. Sheet: 15-Apr-11 B1 QSW 2 of 2 Print Date: 12-May-11 If this document is printed it becomes uncontrolled. Check for the latest revision.