(Reference sheet) SPECIFICATION Supplier : Samsung electro-mechanics CL31B333KHHSFNE Samsung P/N : Description : CAP, 33nF, 630V, 10%, X7R, 1206 Product : Multi-layer Ceramic Capacitor A. Samsung Part Number CL 31 B 333 K H H S F N E Series Samsung Multi-layer Ceramic Capacitor 1206 (inch code) L : W : Size 3.20 0.20 1.60 0.20 Dielectric X7R Inner electrode Ni Capacitance 33 nF Termination Soft termination Sn 100% Capacitance 10 % Plating (Pb Free) tolerance Product Product for POWER application Rated Voltage 630 V Special Reserved for future use Thickness 1.60 0.20 Packaging Embossed Type, 7 reel B. Structure & Dimension Dimension( ) Samsung P/N LTW BW CL31B333KHHSFNE 3.20 0.20 1.60 0.20 1.60 0.20 0.50 0.30C. Samsung Reliablility Test and Judgement Condition Judgement Test condition 1 10% / 1.00.2Vrms Capacitance Within specified tolerance *A capacitor prior to measuring the capacitance is heat Tan (DF) 0.025 max. treated at 150 +0/-10 for 1hour and maintained in ambient air for 242 hours. Insulation 10,000Mohm or 500Mohm 50050 Vdc 605 sec. Resistance Whichever is smaller Appearance No abnormal exterior appearance Microscope (10) 150% Withstanding No dielectric breakdown or of the rated voltage Voltage mechanical breakdown Temperature X7R Characteristics (From -55 to 125 , Capacitance change should be within 15%) Adhesive Strength No peeling shall be occur on the 500gf, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : within 12.5% Bending to the limit (1) with 1.0mm/sec. Solderability More than 95% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455 , 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : within 7.5% Solder pot : 2705 , 101sec. Soldering Heat Tan , IR : initial spec. Vibration Test Capacitance change : within 5% Amplitude : 1.5mm Tan , IR : initial spec. From 10 to 55 (return : 1min.) 2hours 3 direction (x, y, z) Moisture Capacitance change : within 12.5% With rated voltage Tan : 0.05 max Resistance 402 , 90~95%RH, 500+12/-0hrs IR : 500Mohm or 25Mohm Whichever is smaller Capacitance change : within 12.5% With 120% of the rated voltage High Temperature Resistance Tan : 0.05 max Max. operating temperature IR : 1,000Mohm or 50Mohm 1,000+48/-0hrs Whichever is smaller Temperature Capacitance change : within 7.5% 1 cycle condition Cycling Tan , IR : initial spec. Min. operating temperature 25 Max. operating temperature 25 5 cycle test The reliability test condition can be replaced by the corresponding accelerated test condition. D. Recommended Soldering method : Reflow ( Reflow Peak Temperature :250 , 6 sec max.) Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.