BLM18HD102SH1D

Reference Only Spec. No. JENF243A-9104G-01 P.1/9 GHz Noise Suppression Chip Ferrite Bead BLM18HSH1 Murata Standard Reference Specification AEC-Q200 1. Scope This reference specification applies to Chip Ferrite Bead for Automotive Electronics BLM18H SH Series based on AEC-Q200. 2. Part Numbering (ex.) BL M 18 HG 601 S H 1 D (1) (2) (3) (4) (5) (6) (7) (8) (9) (1)Product ID (6)Performance (2)Type (7)Category(for Automotive Electronics) (3)Dimension (L) (8)Numbers of Circuit (4)Characteristics (9)Packaging (D:Taping ) (5)Typical Impedance at 100MHz 3. Rating DC Resistance Impedance ( ) ( max. ) Rated (Under Standard Testing Condition) (*1) (refer to Current ESD Rank (*1) (refer to below comment) Customer MURATA below comment) (mA) Remark 1C:1kV Part Number Part Number Initial Values at 1GHz Values After at 100MHz at at Testing Typical 85 125 BLM18HG471SH1D 47025% 400 min. 600 200 0.85 0.95 For general BLM18HG601SH1D 60025% 450 min. 700 200 1.0 1.1 use BLM18HG102SH1D 100025% 750 min. 1000 100 1.6 1.7 BLM18HD471SH1D 47025% 700 min. 1000 100 1.2 1.3 For BLM18HD601SH1D 60025% 850 min. 1200 100 1.5 1.6 high speed 1C signal line BLM18HD102SH1D 100025% 1100 min. 1700 50 1.8 1.9 BLM18HE601SH1D 60025% 300 min. 600 800(*2) 600(*2) 0.25 0.30 For BLM18HE102SH1D 100025% 500min. 1000 600(*2) 500(*2) 0.35 0.40 power line BLM18HE152SH1D 150025% 750min. 1500 500(*2) 400(*2) 0.50 0.55 Operating Temperature : -55C to +125C Storage Temperature : -55C to +125C (*1) Standard Testing Conditions Unless otherwise specified In case of doubt Temperature : Ordinary Temp. (15 C to 35 C ) Temperature : 20C2 C Humidity : Ordinary Humidity (25%(RH) to 85%(RH)) Humidity : 60%(RH) to 70%(RH) Atmospheric pressure : 86kPa to 106kPa (Note) As for the Rated current marked with (*2), Rated current Rated Current is derated as right figure at 85C depending on the operating temperature. Rated current at 125C 0 85 125 Operating Temperature (C) MURATA MFG.CO., LTD. Rated Current (A)Reference Only Spec. No. JENF243A-9104G-01 P.2/9 4. Style and Dimensions 1.60.15 0.80.15 Equivalent Circuit Resistance element becomes 0.40.2 () dominant at high frequencies. : Electrode Unit Mass (Typical value) 0.005g (in mm) 5. Marking No marking. 6. Specifications 6-1. Electrical Performance No. Item Specification Test Method 6-1-1 Impedance Meet item 3. Measuring Frequency : 100MHz1MHz , 1GHz1MHz Measuring Equipment : KEYSIGHT 4291A or the equivalent Test Fixture : KEYSIGHT 16192A or the equivalent 6-1-2 DC Resistance Meet item 3. Measuring Equipment : Digital multi meter *Except resistance of the Substrate and Wire 6-2. Mechanical Performance (based on Table 13 for FILTER EMI SUPPRESSORS/FILTERS) AEC-Q200 Rev.D issued June. 1 2010 No. AEC-Q200 Murata Specification / Deviation Stress Test Method 3 High 1000hours at 125 deg C Meet Table A after testing. Temperature Set for 24hours at room Table A Exposure temperature, then measured. Appearance No damage Impedance Change Within 30% (at 100MHz) DC Meet item 3. Resistance 4 Temperature 1000cycles Meet Table B after testing. Cycling -55 deg C to +125 deg C Table B Set for 24hours at room Appearance No damage temperature, then measured. Impedance Within 30% Change (BLM18HE (at 100MHz) Within50% DC Meet item 3. Resistance 5 Destructive Per EIA469 No defects Physical Analysis No electrical tests 7 Biased Humidity 1000hours at 85 deg C, 85%RH Meet Table B after testing. Apply max rated current. 8 Operational Life Apply 125 deg C 1000hours Meet Table B after testing. Set for 24hours at room temperature, then measured 9 External Visual Visual inspection No abnormalities MURATA MFG.CO., LTD. 0.80.15