(Reference sheet) SPECIFICATION CL05B103KO5NNND Supplier : Samsung electro-mechanics Samsung P/N: CAP, 10nF, 16V, 10%, X7R, 0402 Product : Multi-layer Ceramic Capacitor Description : A. Samsung Part Number CL 05 B 103 K O 5 N N N D Series Samsung Multi-layer Ceramic Capacitor 0402 (inch code) L: 1.00 0.05 W: 0.50 0.05 Size Ni Dielectric X7R Inner electrode nF Cu Capacitance 10 Termination Sn 100% Capacitance 10 % Plating (Pb Free) tolerance Product Normal Rated Voltage 16 V Special Reserved for future use 0.50 0.05 Cardboard Type, 13 reel Thickness Packaging B. Structure & Dimension Dimension( ) Samsung P/N LTW BW CL05B103KO5NNND 1.00 0.05 0.50 0.05 0.50 0.05 0.25 0.10C. Samsung Reliablility Test and Judgement Condition Judgement Test condition Capacitance Within specified tolerance 1 10% / 1.00.2Vrms *A capacitor prior to measuring the capacitance is heat Tan (DF) 0.035 max. treated at 150+0/-10 for 1 hour and maintained in ambient air for 242 hours. Insulation 10,000Mohm or 100Mohm Rated Voltage 60~120 sec. Resistance Whichever is smaller Appearance No abnormal exterior appearance Microscope (10) 250% Withstanding No dielectric breakdown or of the rated voltage Voltage mechanical breakdown Temperature X7R Characteristics (From-55 to 125, Capacitance change should be within 15%) Adhesive Strength No peeling shall be occur on the 500gf, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : within 12.5% Bending to the limit (1) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Solder pot : 2705, 101sec. Resistance to Capacitance change : within 7.5% Soldering Heat Tan , IR : initial spec. Vibration Test Capacitance change : within 5% Amplitude : 1.5mm Tan , IR : initial spec. From 10 to 55 (return : 1min.) 2hours 3 direction (x, y, z) Moisture Capacitance change : within 12.5% With rated voltage Resistance Tan : 0.05 max 402, 90~95%RH, 500+12/-0hrs 500Mohm or 25Mohm IR : Whichever is smaller 200% High Temperature Capacitance change : within 12.5% With of the rated voltage Resistance Tan : 0.05 max Max. operating temperature 1,000Mohm or 50Mohm IR : 1000+48/-0hrs Whichever is smaller Temperature Capacitance change : within 7.5% 1 cycle condition Cycling Tan , IR : initial spec. Min. operating temperature 25 Max. operating temperature 25 5 cycle test The reliability test condition can be replaced by the corresponding accelerated test condition. D. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.