DP190

TM Scotch-Weld Epoxy Adhesives DP190 Translucent and Gray Technical Data March 2019 Product Description 3M Scotch-Weld Epoxy Adhesive DP190 Translucent is a 1:1 mix ratio similar to 3M Scotch-Weld Epoxy Adhesive 2216 B/A Translucent but faster curing. 3M Scotch-Weld Epoxy Adhesive DP190 Gray is a 1:1 by volume mix ratio of 3M Scotch-Weld Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties. Available in bulk containers as 3M Scotch-Weld Epoxy Adhesive 2216 B/A. Features 90 minute worklife High shear and peel strength Flexible 1:1 mix ratio Translucent or gray color Note: The following technical information and data should be considered representative Typical Uncured or typical only and should not be used for specification purposes. Physical Properties 3M Scotch- 3M Scotch- Weld Epoxy Weld Epoxy Adhesive DP190 Adhesive Translucent DP190 Gray Base Resins Epoxy/Amine Epoxy/Amine 1 Viscosity , Approximate Base (B) 2,000-8,000 cps 75,000-150,000 cps 75F Accelerator (A) 7,000-15,000 cps 40,000-80,000 cps Net Weight Base (B) 9.3-9.7 11.0-11.4 (Lbs./gal.) Accelerator (A) 8.2-8.6 10.6-11.0 Color Base (B) Clear White (Lbs./gal.) Accelerator (A) Amber Gray Mix Ratio (B:A) By Volume 1:1 1:1 By Weight 1.15:1 1.06:1 2 Worklife 2 gram 80 min. 73F (23C) 20 gram 60 min. 90 min. Footnotes: 1. Viscosity determined using 3M test method C-1D. Procedure involves Brookfield RVF, 7 spindle, 20 rpm and 80F (26C). Measurement taken after 1 minute rotation. 2. Worklife determined using 3M test method C-3180. Procedure involves periodically measuring a 2 gram mixed mass for self- leveling and wetting properties. This time will also approximate the usable worklife in an 3M EPX Applicator mixing nozzle. 3M Scotch-Weld Epoxy Adhesives DP190 Translucent and Gray Note: The following technical information and data should be considered representative Typical Cured or typical only and should not be used for specification purposes. Properties Physical Footnotes: 3M Scotch-Weld 3M Scotch-Weld 3. Tack-free time determined per 3M Epoxy Adhesive Epoxy Adhesive test method C-3173. Involves DP190 Translucent DP190 Gray dispensing 0.5 gram amount of adhesive onto substrate and Color Translucent Gray testing periodically for no Hardness (ASTM D 2240) adhesive transfer to metal spatula. Shore D 35 60 4. Handling strength determined per 2 3M test method C-3179. Time to Worklife 80 minutes 90 minutes handling strength taken to be that 3 Tack-free Time ~ 4 hrs ~ 6 hrs required to achieve a 50 psi OLS strength using aluminum 4 Time to Handling Strength 6 hrs 8-12 hrs substrates. 5 Full Cure Time 14 days 7 days 5. The cure time is defined as that 6 time required for the adhesive to Elongation 120% 30% achieve a minimum of 80% of the 6 Tensile Strength 2750 psi 3500 psi ultimate strength as measured by aluminum-aluminum OLS. 6. Tensile and Elongation. Used Thermal procedure in 3M test method C-3094/ATSM D 882. Samples 3M Scotch- 3M Scotch- were 2 in. dumbbells with .0125 in. Weld Epoxy Weld Epoxy neck and .030 in. sample Adhesive DP190 Adhesive thickness. Separation rate was 2 inches per minute. Samples cured Translucent DP190 Gray Weight Loss by Thermal Gravimetric 1% 390F (199C) 1% 477F (247C) 2 hrs RT plus 2 hrs/ 160F (71C). 7 Analysis (TGA) 5% 594F (312C) 5% 639F (337C) 7. Weight loss by TGA reported as Thermal Coefficient of Expansion (TCE) that temperature at which 5% 8 -6 weight loss occurs by TGA in air by TMA ( x 10 units/unit/C) at 5C rise per minute per ASTM Below Tg 86 (41-68F 62 (41-68F 1131-86. 5-20C range) 5-25C range) 8. TCE determined using TMA Above Tg 166 (167-284F 177 (167-284F Analyzer using a heating rate of 75-140C range) 65-140C range) 50F (10C) per minute. Second heat values given. Glass Transition Temperature 9 (Tg) by DCS 9. Glass Transition Temperature (Tg) determined using DSC Analyzer Onset 50F (10C) 45F (7C) with a heating rate of 68F (20C) Mid-Point 80F (27C) 68F (20C) per minute. Second heat values 10 Thermal Conductivity given. ( 110F on .250 in. samples) 10. Thermal conductivity determined 2 BTU - ft./ft. - hr. - F) .079 .220 using ASTM C177 and C-matic -3 -2 Cal./sec. - cm - C) .39 x 10 90.9 x 10 Instrument using 2 in. diameter samples. Watt/m - C .136 .381 11 11. Thermal shock resistance run per Thermal Shock Resistance 3M test method C-3174. Involves Potted Washer Olyphant Test Pass 5 cycles Pass 5 cycles potting a metal washer into a 2 in. (3M ITSD Test Method C-3174 without cracking without cracking x 0.5 in. thick section and cycling +100C air to -50C liquid ) this test specimen to colder and colder temperatures. Electrical 3M Scotch- 3M Scotch- Weld Epoxy Weld Epoxy Adhesive DP190 Adhesive Translucent DP190 Gray Dielectric Constant 1 KH 73F (23C) 6.2 6.5 Z (ASTM D 150) Dissipation Factor 1 KH 73F (23C) 0.16 0.09 Z (ASTM D 150) Dielectric Strength 875 volts/mil 830 volts/mil (ASTM D 149) Sample Thickness Approx. 30 mil. 10 12 Volume Resistivity 7.5 x 10 ohm-cm 5.0 x 10 ohm-cm (ASTM D 257) - 2 -